Evaluating the Effects of Anode Porous Transport Layer on the Performance and Durability of Anion Exchange Membrane...

As anion exchange membrane systems have emerged as a competitive low temperature electrolysis technology, research has expanded to other components and device integration. In this study, nickel (Ni) and stainless steel (SS)-based porous transport layers (PTLs) are investigated in membrane electrode assemblies (MEAs). Compared to MEAs using Ni, the SS PTL shows higher performance due to less kinetics and residual loss and possibly due to a combination of iron mobility improving oxygen evolution reactivity and electron conduction pathways, as well as higher porosity increasing site access. Voltage decay rates of approximately 144 and 115 μV/h, respectively, for the Ni and SS PTLs are found, although the long-term durability and lifetime implications are convoluted. Voltage breakdown analysis confirms that both PTLs saw significant increases in residual loss possibly due to catalyst/PTL property changes that affected electronic, ionic, and mass transport pathways. For the Ni PTL, a higher proportion of the losses were due to cell kinetics; comparatively, more of the SS PTL losses were due to increases in the high frequency resistance. The experimental findings presented here provide insights on the impact of the PTL materials and their properties.