Gamma Radiation Effects in Amorphous and Crystalline Polyaryletherketones

This work investigates the effect of gamma radiation on chain scission and crosslinking in polyaryletherketone (PAEK) thermoplastic filaments, namely, polyetheretherketone (PEEK) and polyetherketoneketone (PEKK) that is either semicrystalline (PEKK-c) or highly amorphous (PEKK-a). The PAEK thermoplastic filaments were exposed to total ionizing doses (TID) of gamma radiation from 1 to 8 MGy in the Gamma Irradiation Facility at Sandia National Laboratories. A combination of thermal and FT-IR spectral analysis of the irradiated specimens was used to study the chain scission and crosslinking behavior between PEEK, PEKK-c, and PEKK-a. Crystallinity decreased with increased TID and melt enthalpy decreased. Despite clear indications of changes to melt and crystallization behavior, any change to the glass-transition temperature was minor until a post-irradiation thermal annealing occurred, which caused an increase in crystallinity. Gamma radiation impacted PEKK-a more due to the lower degree of initial crystallinity, where a reduction in melt enthalpy, crystallinity, and crystallization kinetics was observed. Despite these effects, the ability to achieve a higher degree of crystallization (X _c < 20%) by annealing was not affected. The results presented here provide important insight into the performance of a class of commercialized PEKK thermoplastics exposed to a harsh radiation environment.