Multiple Twin Boundaries in Co-Free Li-Rich Mn-Based Cathodes Constructed by Na-Assisted Sol-Gel Synthesis for...

Cobalt-free Li-rich Mn-based layered oxides are promising cathode materials for next-generation lithium-ion batteries because of their high capacity and reduced reliance on cobalt resources. However, their practical application is still limited by low initial Coulombic efficiency, sluggish reaction kinetics, severe voltage decay, and progressive structural degradation during cycling. In this work, a Na-assisted sol-gel strategy was developed to construct a cobalt-free Li-rich Mn-based cathode with multiple twin boundaries, and the optimized sample with the composition of Li_1.13Na_0.06Mn_0.594Ni_0.219O₂ was denoted as SG-TB. Unlike conventional surface coating or elemental doping, this strategy focuses on regulating the bulk crystal framework through crystallographic defect engineering. Structural characterizations indicate that SG-TB contains repeatedly distributed twin-boundary-related interfaces, supporting the presence of multiple twin boundaries within the layered cathode. Benefiting from this structural feature, SG-TB delivers an initial Coulombic efficiency of 96%, an initial discharge capacity of 256 mAh/g, a discharge capacity of 167 mAh/g at 5 C, and a capacity retention of 77% after 200 cycles at 1 C. Further analyses suggest that the multiple twin boundaries help reduce electrochemical polarization, enhance Li⁺ diffusion kinetics, and improve structural retention during cycling. This work demonstrates that Na-assisted multiple twin-boundary engineering is an effective strategy for improving the reaction reversibility and structural stability of cobalt-free Li-rich Mn-based cathodes.