Research on Carbonation Resistance of Modified/Non-Portland Cements in Carbon Capture, Utilization, and...

Under the global carbon-neutrality target, the technology of carbon capture, utilization, and storage-enhanced oil recovery (CCUS-EOR) faces a severe challenge of carbonation-induced degradation of oil-well cement in harsh downhole environments. Traditional cement suffers serious structural failure under high-temperature and high-pressure CO₂ conditions, whereas single-nanoparticle or polymer modification cannot meet long-term safety requirements. Meanwhile, the comparative study between the "matrix modification strategy" and the "cement system replacement strategy" is still insufficient under real CCUS-EOR conditions. In this study, experimental investigations including macroscopic performance testing, phase analysis, and multi-scale microstructural characterization were conducted. This study systematically evaluates the carbonation resistance of polyaniline@titanium dioxide-modified cement (P@T) and calcium aluminate phosphate cement (CAP). The results show that the carbonation resistance follows the descending order: CAP > P@T > silica-fume-containing Class G oil-well cement (PT). CAP seems to demonstrate a potential "corrosion-induced densification" effect. After 90 days of corrosion, its compressive strength increases to 62.5 MPa, and its permeability decreases to 13.3% of the initial value, indicating continuously improved performance. P@T indicates the possible decoupling of high carbonation degree (CaCO₃ content of 25.26%) and microstructural stability through a structural regulation mechanism of "physical filling-homogeneous distribution of carbonation products". In contrast, PT undergoes complete structural failure after 60 days. This study fills a gap in comparative evaluation between modification and replacement schemes, reveals the multi-scale structural regulatory effects of P@T and the intrinsic stability of CAP, and provides two reliable cement solutions-"modification enhancement" and "system replacement"-for CCUS-EOR environments. The scientific validity is demonstrated through multi-scale characterization, offering key theoretical and technical support for ensuring long-term wellbore integrity.