Preparation and Properties of Transparent, Thermally Insulating, and Flexible SiO₂ Aerogels

SiO₂ aerogels are promising candidates for energy-efficient glazing because of their low thermal conductivity and optical transparency; however, conventional formulations often fail to reconcile optical, thermal, and mechanical performance. This work aimed to resolve this bottleneck via controllable sol-gel synthesis and ambient pressure drying. Using methyltrimethoxysilane (MTMS) as the single silicon source, this study systematically explored the effects of alkaline catalyst type, water-to-MTMS ratio, and surfactant selection, and further developed an MTMS-dimethyl dimethoxy silicane (DMDMS) composite silicon source. Tetramethylammonium hydroxide (TMAOH) catalysis, a water-to-MTMS molar ratio of 7:1, and Pluronic F-127 (F127) surfactant yielded a uniform, hydrophobic aerogel with 93.50% porosity and 89.74% transmittance at 800 nm. The optimized composite system (MTMS:DMDMS = 9:1, 6 mL water, 2.0 g F127) enhanced compressive strength by 22.4% relative to pure MTMS aerogel, with 70.15% visible transmittance and thermal conductivity of 0.027 W/(m·K). These results demonstrate that multi-parameter formulation control can achieve a practical balance among mechanical robustness, optical transparency, and thermal insulation. This study provides a theoretical and process foundation for the engineering application of high-performance transparent thermal insulation materials.