Lamellar-Structured Al₂O₃-SiO₂ Nanofibrous Aerogels with Favorable Compression Resilience for Efficient...

Ceramic nanofiber-based materials have wide applicability in high-temperature management and protection. The transformation of conventional two-dimensional ceramic nanofibrous membranes into three-dimensional nanofiber-based bulks can effectively improve their thermal insulation performance and expand their range of applications. Herein, lamellar-structured Al₂O₃-SiO₂ nanofibrous aerogels (LASO NFAs) with varying inorganic binder contents were prepared via a sequence of processes involving face-to-face stacking, impregnation, and calcination, using flexible Al₂O₃-SiO₂ nanofibrous membranes (ASO NFMs) as building units and aluminum dihydrogen phosphate as an inorganic binder. Varying the inorganic binder content in the aerogel matrix enables effective control over the compressive properties and interlayer spacing of the resulting aerogels. Specifically, the optimized LASO-20 NFAs demonstrated relatively good compression resilience, with a plastic deformation of 22.1% after undergoing 500 compressive cycles at a compressive strain of 50%. Moreover, profiting from the high-temperature resistance of ASO NFMs and substantial air content present within nanofiber interlayers, the LASO-20 NFAs with a thickness of 20 mm could effectively insulate against surface temperatures of 1000 °C down to 224 °C. Moreover, LASO-20 NFAs exhibited a room-temperature thermal conductivity of approximately 0.043 W·m^-1·K^-1, illustrating a favorable high-temperature thermal insulation characteristic. Furthermore, the LASO-20 NFAs presented promising service performance in extreme environments, providing a novel perspective in the development of new types of ceramic aerogels.