Preparation of Magnetic Biochar Derived from Spent Mushroom Substrate and Its Adsorption and Regeneration Performance...

Nitrogen and phosphorus are the primary pollutants responsible for eutrophication in water bodies, and their effective removal is crucial for water environmental protection. Biochar, owing to its porous structure and surface functional groups, exhibits excellent adsorption performance for nitrogen and phosphorus, which can be significantly enhanced through metal modification. In this study, magnetic biochar (MBC) was prepared from spent mushroom substrate via FeCl₃ impregnation and microwave pyrolysis, and its adsorption performance for NH₄⁺ and PO₄^3- was systematically evaluated. The physicochemical properties of MBC were characterized using scanning electron microscopy, thermogravimetric analysis, specific surface area and pore structure analysis, vibrating sample magnetometry, and Fourier transform infrared spectroscopy. The results showed that the saturated magnetization of MBC was 7.86 emu/g, the specific surface area was 37 m²/g, and the material exhibited a mesoporous structure with high thermal stability. The adsorption process followed pseudo-second-order kinetics, and the mechanisms involved electrostatic interactions, surface complexation, and pore filling. Isotherm studies indicated that the maximum adsorption capacities of MBC for NH₄⁺ and PO₄^3- were 16.25 mg/g and 14.99 mg/g, respectively. Thermodynamic analysis revealed that the adsorption of NH₄⁺ was exothermic, whereas that of PO₄^3- was endothermic. Furthermore, MBC maintained an adsorption efficiency of up to 93% after ten adsorption-desorption cycles, demonstrating excellent reusability.