Fabrication of Breathable Coating and Its Hydrophobization Applied for the Rust Stabilization of Weathering Steels

The self-formed rust layer is significant for weathering steels because their corrosion resistance in a marine atmospheric environment mainly relies on the stability, uniformity and compactness of the rust layer. However, the initial stage of rust formation is vulnerable and prone to being disturbed by the external environment, compromising the protectiveness of the rust layer at a later stage. Therefore, weathering steel often requires the application of rust stabilization techniques. This study has developed a waterborne polyurethane (WPU)-based coating incorporated with mesoporous/hollow SiO₂ nanoparticles, acting as the primary components for the construction of pathways for gaseous H₂O and O₂, as well as for Cl^- dissolved in moisture, while blocking liquid water. Salt spray was applied to accelerate the rust formation process, and rust can form beneath the coating, which provides shelter for rust formation against the external environment. Hexamethyldisilazane (HMDS) was applied to further hydrophobize the nanoparticles, and a hydrophobic surface with self-cleaning properties was achieved. The hydrophobized and non-hydrophobized coatings with different thicknesses (10-80 µm) were systematically compared: the morphology of the rust layer and coating surface after salt spray was investigated, the ability of the rust layer to inhibit chloride ingress was compared, and the electrochemical behaviors were analyzed. This study presents a new strategy for weathering steel rust stabilization that features maneuverability, environmental friendliness and low cost.