The Influence of Fiber Tension and Filament Winding Patterns on the Strength of Thin-Walled Fiber-Reinforced Polymer...

This study investigates the effects of filament winding parameters (tension and mosaic pattern) on the mechanical performance of thin-walled fiber-reinforced polymer composite tubes under internal pressure. The pressure was generated through axial compression of an elastomeric insert, providing a controlled alternative to conventional hydrostatic burst testing. Tubes were manufactured with different combinations of winding tension (10-50 N) in the ±55° and hoop layers. Within the ±55° layer, several mosaic pattern configurations were tested. Structural responses were evaluated using pressure testing, Digital Image Correlation (DIC), and Scanning Electron Microscopy (SEM). 20 N was identified as the most efficient tension level, improving interlaminar integrity and increasing hoop tensile strength by approximately 8-13%. Specimens with a hoop layer failed abruptly by hoop-dominated brittle fracture, characterized by longitudinal splitting and fiber rupture in the circumferential direction. Among the investigated mosaic configurations, the 3/3 pattern demonstrated the most efficient structural response-the mean hoop tensile strength (1088 ± 43 MPa) was approximately 31-40% higher than that of the remaining configurations (722-798 MPa). Overall, the results indicate that both winding tension and mosaic pattern influence the failure pressure, with optimized configurations contributing to improved pressure resistance and structural consistency.