Hierarchical battery-type MnFe₂O₄@Ni(OH)₂ spinel ferrite-hydroxide nanostructures for high-performance...

This study reports the synthesis and characterization of MnFe₂O₄, Ni(OH)₂, and MnFe₂O₄@Ni(OH)₂ electrodes grown on Ni foam through a facile hydrothermal synthesis method. X-ray diffraction and Raman analyses confirm the coexistence of cubic spinel MnFe₂O₄ and mixed α/β-Ni(OH)₂ phases in the composite, while field-emission scanning electron microscopy reveals a hierarchical morphology, where Ni(OH)₂ nanosheets uniformly coat the MnFe₂O₄ nanoparticles, enhancing surface exposure and ion accessibility. Electrochemical investigations demonstrate that all electrodes exhibit battery-type behavior, with well-defined redox peaks and plateau regions in the cyclic voltammetry and galvanostatic charge-discharge curves. The MnFe₂O₄@Ni(OH)₂ composite achieves a significantly higher specific capacity (572.95 C g^-1 at 2 mA cm^-2) and superior rate performance compared to the individual components. This is attributed to the synergistic interaction between the conductive MnFe₂O₄ core and the electroactive Ni(OH)₂ shell. In symmetric supercapacitor devices, the MnFe₂O₄@Ni(OH)₂ electrode delivers excellent energy storage performance (20.16 Wh kg^-1 at a power density of 395.4 W kg^-1), with improved charge transfer and remarkable cycling stability (140.04% retention over 3000 cycles). The findings indicate that combining spinel ferrites with layered hydroxides in a hierarchical architecture offers a promising strategy for designing high-performance, battery-type supercapacitors.