Cr/AlCrNbSiTiN/AlCrNbSiTiO Gradient Nano-Multilayer Coatings with Excellent Solar Absorption and Photothermal...

High-entropy alloys exhibit a broad light-responsive spectrum, spanning the ultraviolet to visible range, and their light absorption coefficient is significantly higher than that of traditional binary oxides. Cr/AlCrNbSiTiN/AlCrNbSiTiO gradient nano-multilayer coatings with excellent solar selective absorption properties are prepared using ion source enhanced magnetron sputtering. The effects of thickness of the absorption layer of AlCrNbSiTiN (3/4/5 min, denoted as S-3/4/5) are systematically investigated. It is worth noting that nano-multilayer coatings of S-3, S-4, and S-5 exhibit nearly perfect absorption rates of 0.9847, 0.9888, and 0.9879, respectively. The TEM images shows clear interfaces between the various coating layers, exhibiting a gradient structure that combines nanocrystalline and amorphous characteristics. From the substrate to the surface, there is an increase in the content of nanocrystalline phases, coarsening of grain sizes, and a decrease in the amount of amorphous phases. The primary absorption layer of AlCrNbSiTiN displays a typical face-centered cubic nitride structure. The XPS analysis reveals that the high-valent oxides (Nb⁵⁺, Cr⁶⁺) ensure thermal stability, whereas mixed valence states of Cr³⁺/Cr⁶⁺ may enhance visible light absorption through multi-electron transitions. This study analyzes how both the thickness of absorbing layers and high-temperature annealing affect the optical properties and photothermal conversion performance of AlCrNbSiTiN-based high-entropy coatings, which provides valuable insights for developing high-performance selective absorbers.