Physical and Mechanical Characterisation of 3D-Bioprinted Hydrogels for Dental Applications: A Scoping Review

Recent advances in three-dimensional (3D)-bioprinted hydrogels show promise for overcoming the limitations of conventional techniques for dental tissue regeneration. This scoping review systematically analyses the physical, mechanical, and rheological properties of these hydrogels in dental applications, aiming to identify knowledge gaps, limitations, and current and future directions for advancing and translating hydrogel-based 3D bioprinting in dentistry. In accordance with PRISMA-ScR guidelines, a comprehensive literature search was conducted across Ovid, PubMed, EBSCOhost, and Web of Science up to January 2026. Included studies focused on (i) 3D-bioprinted hydrogels, (ii) quantitative characterisation, and (iii) dental tissue engineering. A total of twenty-one studies met the inclusion criteria. The findings revealed substantial variability in formulations and properties. Gelatine-based hydrogels reinforced with β-tricalcium phosphate demonstrated the highest compressive strength within the range of cancellous bone, whereas GelMA/PEGDA composites exhibited tunable stiffness suitable for soft tissue applications. Extrusion-based bioprinting emerged as the predominant method, with photocrosslinking and ionic crosslinking as the primary gelation techniques. Biodegradation rates varied notably with composition and regenerative objectives. This review uniquely consolidates the physical, mechanical, and rheological evaluations of 3D-bioprinted hydrogels for dental applications. The review highlights critical gaps in methodological standardisation and validation, emphasising the importance of biomaterial selection to optimise scaffolds and regenerative outcomes in periodontal, bone, and pulp tissue engineering.