Physics-Informed Optimization for the Sub-Feature-Scale Fabrication of Hollow Microneedles via Digital Light...

To overcome low bioavailability and high trauma in inner ear therapies, targeted delivery across the round window membrane (RWM) via hollow microneedles (HMNs) offers a promising solution. However, the fabrication of high-aspect-ratio, small-size HMNs remains challenging. This study demonstrates the successful fabrication of small-outer-diameter HMNs using a 10 μm resolution digital light processing (DLP) system. Finite element analysis (FEA) identified a double tangent-arc transition as the optimal structural design for minimizing stress concentration. To manage the heightened parameter sensitivity at sub-feature-scale fabrication, a corrected curing index (CCI) model was established via a physics-informed regression approach incorporating polymerization kinetics and nonlinear spatial intensity distribution, achieving high fitting accuracy (R² > 0.96). Under optimized parameters, the fabricated HMNs possessed mean dimensions of 805.13 μm in height, 37.54 μm in inner diameter, and 79.36 μm in outer diameter. Compressive tests exhibited a robust structural strength of up to 141 mN per needle following post-curing. Combined in silico and in vitro experiments demonstrated excellent penetration performance. Furthermore, the HMNs achieved stable, pressure-dependent delivery with volumetric flow rates rising from 0.14 mL∙min^-1 to 0.39 mL∙min^-1 as driving pressure escalated from 50 kPa to 300 kPa, validating their functional capacity for controlled drug administration.