Preparation of Unburned Lightweight Aggregates via Synergistic Utilization of Red Mud and Multi-Source Solid Wastes...

This study aims to explore the preparation process and properties of unburned lightweight aggregate using red mud synergistically with fly ash, granulated blast-furnace slag, and other multi-source solid wastes. Curing regimes and alkali-activated systems were controlled. Their effects on physical properties and environmental safety of lightweight aggregate were systematically evaluated. Results show that curing temperature and alkali activator exert significant synergistic effects on physical properties of lightweight aggregates. Steam curing performs better than standard curing. Performance improves with increasing steam temperature. Sodium silicate solution with a modulus of 1.0 is determined as the optimal activator. Under 90 °C steam curing, Sample D2 achieves the best overall performance. Its cylinder compressive strength reaches 6.92 MPa. 1 h water absorption is 14.8%. Softening coefficient is 0.93. Porosity is as low as 31.07%. Microscopic analysis reveals that higher curing temperature significantly accelerates the hydration reaction of the RMLWA system. It promotes the formation of abundant cementitious products such as C-S-H gel. These products fully fill internal pores and microcracks of the aggregate. A dense three-dimensional network skeleton structure is finally formed. For environmental safety, heavy metal leaching concentrations of steam-cured samples are generally lower than those of standard-cured samples. This study realizes high-value resource utilization of industrial solid wastes. It also provides a new technical route for the development of green building lightweight aggregate.