Accuracy Analysis of Holes Drilled in Ductile Cast Iron with an HSS Helical Drill Bit

Controlling macro-geometrical errors in the dry drilling of ductile cast iron remains a critical challenge for sustainable and cost-efficient automotive component manufacturing. This paper investigates the influence of cutting speed (v_c) and feed per revolution (f_n) on the dimensional and shape accuracy of holes drilled in EN-GJS-500-7 ductile cast iron using an HSS DIN 338 helical drill (Ø 11.8 mm, Ceratizit) on an AVIA VMC800 CNC milling centre. A one-factor-at-a-time (OFAT) experimental design was applied: the feed effect was evaluated at v_c = 10 m/min with f_n ∈ {0.10, 0.15, 0.20} mm/rev, while the speed effect was evaluated at f_n = 0.20 mm/rev with v_c ∈ {10, 25, 30} m/min. Cutting forces, torques, and vibration accelerations were recorded using an HBM MSC 10 transducer and a PCB 356A01 tri-axial accelerometer. Hole geometry was assessed on a Zeiss Contura G2 coordinate-measuring machine (CMM), and surface texture was evaluated with a TOPO 01P contact profilometer. The expanded measurement uncertainty (k = 2) was estimated based on duplicate test specimens. All drilled holes fell within the IT12 dimensional tolerance (PN-EN 22768-1:1999 grade c), with diameter oversizes ranging from +0.26 mm to +0.46 mm relative to the nominal bore. Cutting speed was identified as the dominant factor affecting both diameter oversize and cylindricity, which increased by 60% (from 0.10 to 0.16 mm) as v_c rose from 10 to 30 m/min. Vibration accelerations increased nonlinearly between v_c = 25 and 30 m/min (by a factor of 2.5×), indicating an approach to a structural resonance condition. The lowest surface roughness (R_a = 6.6 µm) was obtained at v_c = 25 m/min. These findings establish clear physical baselines for tool deflection limits, demonstrating that managing dynamic process stability is vital for optimising macro-geometrical accuracy in the dry machining of cast iron alloys.