Microstructure and Mechanical-Tribological Properties of HVOF-Sprayed (WC-Co+Ni) Coatings on Ductile Cast Iron

High Velocity Oxy-Fuel (HVOF) thermal spraying enables the deposition of dense coatings with low porosity, high hardness, and good fracture resistance. Tungsten carbide-cobalt (WC-Co) coatings are widely used in industrial and aerospace applications due to their excellent wear resistance; however, improving crack resistance and coating-substrate adhesion remains a key challenge. In this study, WC-Co+Ni composite coatings were deposited on ductile cast iron, with emphasis on the role of Ni addition in controlling microstructure development under HVOF conditions. Microstructural characterization was performed using optical, scanning, and transmission electron microscopy (OM, SEM, TEM), while phase composition and chemical analysis were determined by X-ray diffraction (XRD) and energy-dispersive spectroscopy (EDS). The coatings exhibited a dense, low-porosity microstructure composed of fine WC and W₂C carbides embedded in a Co-Ni binder, with locally nanocrystalline regions. XRD analysis confirmed WC and W₂C as the dominant phases, with weak reflections corresponding to the η-phase (Co₆W₆C), indicating local decarburization. The addition of Ni increases the fraction of the transient liquid phase during particle flight, enhancing carbide dissolution and mass transport in the binder, which accelerates decarburization kinetics and promotes η-phase formation. Simultaneously, Ni modifies the binder into a more ductile Co-Ni matrix, reducing the detrimental effect of brittle η-phase on coating integrity. Mechanical and tribological testing (instrumented indentation and scratch testing) demonstrated improved crack resistance, wear resistance, and adhesion. The results show that Ni addition enables process-driven microstructural tailoring of HVOF-sprayed WC-Co coatings, leading to enhanced performance despite the presence of η-phase.