The Interfacial Interaction of Functional Liquid Polyisoprene Rubber in SSBR/Silica Composite

Silica dispersion in rubber matrices remains a critical issue due to the polarity mismatch between silica and the rubber phase. This study aimed to synthesize functionalized liquid polyisoprene rubber (F-LIR) and evaluate its role in improving the interfacial interaction between silica and solution styrene-butadiene rubber (SSBR). F-LIR was synthesized by introducing an alkoxysilane-containing functionalizing agent at the termination stage of anionic polymerization. Fourier transform infrared spectroscopy (FT-IR) and proton nuclear magnetic resonance spectroscopy (¹H-NMR) were used to confirm the successful introduction of silyl groups at the chain ends of liquid polyisoprene. The optimal loading of F-LIR in SSBR was evaluated through bound rubber content, dynamic mechanical analysis, and mechanical performance testing. The results demonstrated that F-LIR improved the tensile strength, modulus at 300% elongation, and bound rubber content of SSBR composites. These enhancements are attributed to the reaction between the silyl groups of F-LIR and surface hydroxyl groups of silica, together with the co-crosslinking interaction between F-LIR and SSBR. The composites containing 4 phr F-LIR exhibited the best overall balance of properties. This study provides a novel method for synthesizing F-LIR, which bridges silica and the rubber matrix by enhanced filler-rubber interactions at the filler-rubber interface.