Uniaxial Compression Failure Behavior and Energy Evolution of Sandstone-Marble Waste Powder Concrete Composites

Sandstone-marble waste powder concrete composite structures serve as common load-bearing systems in tunnels, underground caverns, and similar engineering projects, where the interface roughness characteristics directly govern their overall stability and service safety. To investigate the influence of interface roughness on the failure behavior of the composite, four groups of sandstone-concrete composite specimens made with marble waste powder concrete were prefabricated with different joint roughness coefficients (JRC = 0, 7.84, 17.99, 20.79). The concrete matrix was prepared with marble waste powder incorporated at 25 wt% of the total binder, corresponding to 20.45 wt% of the total mixture, and the water-to-binder ratio was 0.20. Uniaxial compression tests were conducted with synchronous acoustic emission (AE) and digital image correlation (DIC) monitoring to examine the roughness-dependent mechanical response, energy evolution, damage activity, and strain localization of the composites. The results show that the peak stress and elastic modulus of the composite increase continuously with increasing JRC. When JRC increases from 0 to 20.79, the peak stress increases by 170.3% and the elastic modulus increases by 201.1%. The energy evolution mechanism transitions from progressive damage with gradual energy dissipation at low roughness to a three-stage mode at high roughness, characterized by initial frictional energy dissipation, intermediate energy storage, and rapid elastic energy release and dissipated energy increase near failure. DIC results further reveal that increasing interface roughness suppresses interfacial shear slip and promotes tensile-dominated strain localization, whereas excessive roughness may induce local stress concentration around asperities and increase the tendency toward abrupt post-peak instability, the failure mode changes from mixed tensile-shear failure with obvious interfacial slip to tensile-dominated failure.