Utilization of Municipal Solid Waste Ash in Concrete Blends in Israel Part B: Combustion in a Semi-Industrial...

This study (Part B) examines the potential utilization of municipal solid waste (MSW) ash, produced in a semi-industrial incinerator in Israel, as a partial substitute for cement and natural sand in industrial concrete mixtures. The ash was produced at the temperature range 600-850 °C, and the ash was characterized using XRD and SEM to determine its mineralogical composition and morphology. The results indicate that ash composition is dominated by calcium-rich phases, with hatrurite (Ca₃SiO₅) representing approximately 51-66 wt.% of the identified crystalline phases, along with calcite, MgO, and silica phases. The ash consists of irregular, porous particles with a broad distribution. Concrete performance was evaluated in both fresh and hardened states. In terms of fresh concrete properties, it is observed that concrete containing ash showed improved workability, better workability retention, and better concrete density compared to concrete without ash. In terms of hardened concrete properties, the use of MSW ash as a partial sand replacement preserved the mechanical performance of the concrete, with compressive strength remaining within approximately 2% of the reference mixture. These findings suggest that semi-industrially produced MSW ash is more suitable as a fine aggregate replacement than as a supplementary cementitious material and represents a promising route for reducing landfill disposal and promoting circular economy practices in the construction industry.