Microstructure and Mechanical Properties of In Situ Al₃Zr/Al-5Cu-0.6Mn-0.15Ti Heat-Resistant Aluminum Matrix...

xAl₃Zr/Al-5Cu-0.6Mn-0.15Ti composites were fabricated via an in situ reaction method, and the influence of Al₃Zr content on the microstructure and mechanical properties in both as-cast and T6-treated conditions was systematically investigated. The results reveal that the D0₂₃-Al₃Zr content increases in proportion to the K₂ZrF₆ addition level. Following T6 heat treatment, finely dispersed θ'-Al₂Cu precipitates were formed within the matrix, and the α-Al + θ-Al₂Cu eutectic network dissolved. The blocky Al₃Zr particles underwent spheroidization and could continuously exert a grain boundary pinning effect to suppress grain coarsening. After T6 heat treatment, the 4.5 wt.% Al₃Zr composite exhibited average ultimate tensile strengths of 324.44 MPa at room temperature and 123.38 MPa at 350 °C, corresponding to improvements of 8.56% and 23.31%, respectively, relative to the unreinforced base alloy. Following thermal exposure at 350 °C for 24 h, the composite exhibited less pronounced coarsening of the θ'-Al₂Cu precipitates compared with the base alloy, while the Al₃Zr particles retained their morphological and dimensional stability. Consequently, the reductions in both tensile strength and hardness were smaller than those observed for the base alloy. Analysis indicates that Al₃Zr particles significantly refine the α-Al grains and enhance the alloy's thermal stability. The superior property retention is attributed primarily to the high thermal stability of the Al₃Zr particles, which preserve their dispersion-strengthening contribution at 350 °C, with the reduced θ' coarsening as a contributing factor. The overall strengthening of the composite arises from the combined and largely independent contributions of Al₃Zr particle strengthening and θ'-Al₂Cu precipitation strengthening.