Flexible Polymer-Stabilized Liquid Crystal Films Based on Radical-Promoted Cationic Co-Polymerization of Epoxy...

Polymer-stabilized liquid crystal (PSLC) films are promising for smart window applications because of their transparent-to-scattering switching behavior. However, conventional acrylate-based PSLC films often suffer from poor mechanical robustness and weak interfacial adhesion, limiting their use in flexible devices. Herein, epoxy-based PSLC films have been prepared through radical-promoted cationic photopolymerization using a difunctional epoxy monomer, E6M, and a series of liquid-crystalline monoepoxy monomers, E-nOCB. The effects of alkyl chain parity, chain length, and E6M/E-10OCB ratio on polymer morphology, electro-optical behavior, and peel strength were systematically investigated. Even-numbered E-nOCB monomers favored the formation of regular columnar polymer structures and improved optical contrast, whereas odd-numbered monomers produced more disordered networks with higher peel strength. Among them, the sample prepared with E-10OCB showed a better balance between electro-optical performance and mechanical adhesion. At a fixed total polymer content of 15 wt%, optimizing the E6M/E-10OCB ratio enabled the sample doped with E-10OCB to achieve the highest contrast ratio of 160.91 while increasing the peel strength from 47.28 to 55.69 kPa compared with the sample without E-10nOCB. These results demonstrate that regulating monoepoxy/diepoxy composition and alkyl chain structure is an effective strategy for improving the overall performance of epoxy-based PSLC films for smart windows.