Pyrolysis Kinetics and Thermodynamics of Ambient-Pressure-Dried Silica Aerogels Modified with Tri-, Di- and...

Hydrophobic silica aerogels are widely used as thermal-insulation materials, but the thermal decomposition of their organic surface groups may affect their stability and safety during high-temperature service. In this study, ambient-pressure-dried silica aerogels modified with trimethylsilyl, dimethylsilyl, and methylsilyl groups were prepared and denoted as TSA, DSA, and MSA, respectively, to clarify how the degree of methyl substitution in the surface modifier controls the pyrolysis behavior of hydrophobic silica aerogels. Thermogravimetric analysis at different heating rates was combined with TG-FTIR, a model-free kinetic analysis, a model-fitting analysis and thermodynamic calculation. With decreasing methyl substitution from TSA to MSA, the aerogel framework became denser, the specific surface area decreased, and the contribution of solid-phase heat transfer increased slightly. The main pyrolysis process occurred at 250-800 °C and involved multiple overlapping reactions. The average activation energies of TSA, DSA, and MSA were 241.4, 246.6, and 285.5 kJ/mol according to the Kissinger-Akahira-Sunose (KAS) method and 243.0, 248.2, and 289.0 kJ/mol according to the Flynn-Wall-Ozawa (FWO) method, respectively. The higher activation energy of MSA indicates that the more condensed silica-rich framework and lower organic methyl content improves its resistance to the main degradation process. The model-fitting analysis further suggested an A1/2 mechanism for TSA and A2/5 mechanisms for DSA and MSA. TG-FTIR further confirmed the evolution of CO₂, H₂O, CH₄, and C₂H₄ and revealed distinct gas-release behaviors among the three samples. These results demonstrate that the surface methyl-substitution structure governs the balance between hydrophobic modification, pore-structure preservation, pyrolysis resistance, and volatile-product release, providing a basis for selecting surface modifiers for thermally stable silica-aerogel insulation materials under oxygen-limited high-temperature conditions.