From Solid-Solution Strengthening to Grain Boundary Segregation: A Study on the Mechanism of Magnetic Property...

This study systematically investigates the effects of varying Ni doping levels (1.0-7.0 wt.%) on the microstructure, static magnetic properties, and high-frequency dynamic magnetic performance of Fe-5.5 wt.% Si soft magnetic composites (SMCs). Toroidal core samples were fabricated using powder metallurgy combined with silicone resin coating and high-temperature annealing. The influence of Ni doping on phase composition, morphology, saturation magnetization, coercivity, effective permeability, quality factor, total core loss and its components, and DC bias characteristics was comprehensively evaluated by XRD, SEM, EDS, hysteresis loop testing, and DC bias measurements. The results indicate that an appropriate Ni content (3.0-5.0 wt.%) promotes the formation of α-Fe(Si,Ni) solid solution and (Fe,Ni)₃Si ordered phases, optimizes grain size and structural ordering, enhances saturation magnetization, and reduces coercivity. In contrast, excessive Ni doping (7.0 wt.%) leads to Ni segregation at grain boundaries, forming strong pinning centers that significantly increase coercivity and hysteresis loss. Within the wide frequency range of 1-100 kHz, Ni doping improves the permeability retention under DC bias but reduces the initial effective permeability. Notably, the sample with 5.0 wt.% Ni exhibits the highest quality factor (Q value) across the entire frequency range, demonstrating the best overall performance. This study provides experimental evidence and theoretical guidance for developing high-saturation-resistance, low-loss soft magnetic composites for medium-to-high-frequency applications.