Experimental Investigation of Mechanical Performance and Gamma Radiation Shielding of Hybrid Magnetite-Dolomite...

Nuclear infrastructure requires reliable gamma radiation shielding, for which heavyweight concrete offers a practical, structural solution. Conventional concrete provides poor gamma shielding and heat durability, demanding a denser alternative. Prior studies show that magnetite enhances attenuation and strength, while dolomite improves thermal/mechanical stability, yet findings are dispersed across materials and test conditions. Hybrid magnetite-dolomite concrete requires systematic evaluation for simultaneous optimal gamma shielding and mechanical performance under nuclear conditions. Two mixes were produced by partial replacement of coarse aggregate (Mix 1: 50% magnetite, 25% dolomite; Mix 2: 25% magnetite, 50% dolomite), casted and cured per standard practice with compressive strength measured at 7 and 28 days. Gamma attenuation was quantified using Cs-137 and Co-60. Mix 1 achieved 78.78% attenuation for Cs-137 and 76.86% for Co-60, while Mix 2 reached 77.65% and 74.68%, respectively. At 28 days, peak compressive strengths were 25.8 MPa (magnetite), 22.6 MPa (dolomite), and 20.6 MPa (control), with pre-peak energy capacity ranking as follows: magnetite > dolomite > control. Magnetite increased strength and attenuation but sharpened post-peak softening, whereas dolomite enhanced deformability and energy dissipation with minimal loss in shielding. Hybrid concrete satisfied shielding and strength targets and outperformed conventional concrete, with a magnetite-forward blend offering the best overall protection.