Microscopic Leaching Mechanism of Fly Ash Geopolymer (FAG) Under Coupled Stray Current and Soft Water

Severe electrochemical corrosion and leaching degradation of underground structures are induced by coupled stray current and groundwater in rail transit systems like subways. The microstructural evolution of fly ash geopolymer (FAG) during accelerated leaching was systematically investigated by simulating a coupled direct current (DC) stray current and soft water environment. Pore solution alkalinity and electrolytic cell OH^- concentration were utilized as evaluation indicators, combined with X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and mercury intrusion porosimetry (MIP). Results indicate that substantial OH^- leaching occurs under the coupled stray-current and soft-water exposure, leading to reduced pore-solution alkalinity and changes consistent with the degradation of the N-A-S-H binding network. Consequently, porosity, most probable pore diameter, and the quantity of harmful pores are increased. However, no obvious changes in the major diffraction peaks associated with quartz and mullite were detected within the resolution of the qualitative XRD analysis. Furthermore, a linearly decreasing trend over time is observed for the coupled leaching rate. Mix proportion analysis demonstrates that FAG leaching resistance is improved by reducing the water-to-binder ratio; specifically, superior gel phase content and pore structure are maintained at a ratio of 0.30. Additionally, cumulative OH^- leaching is effectively reduced by decreasing the sodium silicate modulus, with optimal resistance exhibited between 1.0 and 1.2. Concurrently, pore solution alkalinity before and after leaching is significantly elevated by increasing the alkali dosage. This exerts a pronounced inhibitory effect on OH^- leaching, thereby substantially enhancing the overall leaching resistance.