Compressive Stress-Assisted Drilling for Delamination Suppression in C/SiC Composites: Mechanism and Experimental...

Carbon-fiber-reinforced silicon carbide (C/SiC) ceramic matrix composites (CMCs) exhibit substantial application potential in the field of advanced industrial manufacturing, attributed to their inherent superiorities such as high specific strength, excellent high-temperature resistance, and prominent corrosion resistance. Nevertheless, hole-exit delamination is a critical defect in C/SiC composite drilling, which impairs the structural integrity and service reliability of components, restricting their engineering implementation. To address this issue, this study proposes and systematically investigates a compressive stress-assisted drilling method for delamination suppression via applying external compressive stress. Using the delamination factor for quantitative evaluation, comparative experiments were conducted under unassisted drilling, graphite-plate-assisted drilling without preload, and graphite-plate-assisted drilling with varying preload torques. The results indicate that compressive stress significantly mitigates delamination, with a maximum delamination factor reduction rate of 18.29%. Mechanistically, the compressive stress effectively controls delamination by suppressing Mode I crack propagation at the crack tip and elevating the critical strain energy release rate. Furthermore, this work elucidates that the essential role of the graphite plate is to provide a controllable in-plane pre-compressive stress field for the workpiece drilling zone.