Low-Carbon UHPC Incorporating GGBS-Calcium Carbide Slag and Recycled Plastic Fibers: Mechanical Properties,...

Ultra-high-performance concrete (UHPC) typically contains high cement and steel-fiber contents, leading to high cost and carbon emissions. This study developed a low-carbon UHPC by partially replacing cement with industrial solid waste (ISW) composed of ground granulated blast-furnace slag and calcium carbide slag, and by partially replacing steel fibers with recycled plastic fibers (RPF). The effects of ISW and RPF on flowability, mechanical properties, hydration behavior, microstructure, carbon emissions, and raw-material cost were investigated. ISW had a limited influence on flowability, whereas RPF markedly reduced flowability. Appropriate ISW and RPF contents increased flexural and compressive strengths by up to 41.02% and 14.93%, respectively. The 30% ISW-50% RPF mixture provided the highest flexural strength, while 30% ISW-30% RPF achieved the highest compressive strength with acceptable flowability. Hydration heat, XRD, SEM, and FTIR analyses showed that moderate ISW promoted early hydration and C-S-H/C-A-S-H gel formation, whereas excessive ISW caused dilution and reduced matrix compactness. Therefore, 30% ISW-30% RPF is recommended as the balanced formulation, whereas 50% ISW-50% RPF is more suitable for carbon- and cost-sensitive applications and maintains approximately 150 MPa compressive strength.