From Filamentary Failure to Durable Halide Perovskite Memristors

Halide perovskites have emerged as promising materials for memristive devices. While their pronounced electrochemical reactivity and fast ionic mobility enable numerous advantages including low-voltage operation and fast switching, the same features also render perovskite-based memristors vulnerable to metallic shunts and poor endurance, limiting their practical applications. Here, we elucidate both the resistive switching and failure mechanisms in perovskite memristors with a fluorine-doped tin oxide (FTO)/methylammonium lead triiodide (MAPbI3)/Ag structure and demonstrate a strategy to substantially enhance device durability. As opposed to commonly invoked filamentary mechanisms, electrical, structural, and spectroscopic analyses reveal that resistive switching arises from interfacial barrier modulation by reversible Ag redox reactions that drive electrochemical doping/dedoping within the perovskite. Device failure, however, originates from metallic Ag0 filamentation that ultimately forms permanent conductive pathways. Introducing an ultrathin Al2O3 interlayer at the inert-electrode interface improves device endurance by more than 30-fold, exceeding 15,000 switching cycles, without compromising other performance metrics. Interfacial characterization indicates that the Al2O3 layer modifies wettability of Ag deposits, promoting planar island growth rather than through-film filamentation. These findings establish a clear link between interfacial electrochemistry, metal precipitation behavior, and memristor reliability, highlighting inert-electrode interfacial engineering as an effective pathway toward durable perovskite-based memristors.