Enhancing hydrogen storage aspects and energy conversion efficiency in BaSiH6 via A@Ba-site substitution (A = Be, Mg,
Usman Saeed1, Arslan Zulfiqar2, Bassem F Felemban3
1Department of Physics, University of Sargodha 40100 Sargodha Pakistan safdar.nazir@uos.edu.pk +92-334-9719060.
Abstract:
Hydrogen is widely acknowledged as a highly effective potential solution to meet the steadily increasing demand for clean and environmentally friendly energy, where hydridosilicates emerge as an efficient hydrogen storage material. Here, the various physical aspects of BaSiH6 via A@Ba-site substitution (A = Be/Mg/Ca/Sr/Ra) are investigated using first-principles calculations. The stability of these systems was confirmed through formation enthalpy, with values ranging from -30.1 kJ mol-1 H2 (Be@Ba) to -49.1 kJ mol-1 H2 (Sr@Ba), where Ca@Ba (-42.4 kJ mol-1 H2) and the pristine system (-40.9 kJ mol-1 H2) have almost ideal values (-40.9 kJ mol-1 H2) for practical reversibility, indicating tunable thermodynamic stability for all structures. The estimated desorption temperatures (derived from formation enthalpies) for the pristine (292 K) and Mg@Ba/Ca@Ba/Ra@Ba-doped systems (235/303/250 K) fall within the desirable operating window of 233-333 K, which provides a comparative thermodynamic assessment of hydrogen-release behavior rather than exact decomposition temperatures. We observe that the hydrogen storage capacity (C wt%) is a direct function of the dopant's molar mass, with lighter elements significantly boosting C wt% to 5.64/5.26/4.92/4.12/3.53/2.8% for Be/Mg/Ca/Sr/Ba(pristine)/Ra-doped systems, while maintaining volumetric capacities of 64.98/65.58/65.35/62.09/57.91/57.16 gH2 per L. The structural integrity of all structures was rigorously validated through ab initio Molecular Dynamics Simulations at 300 K and mechanical stability checks via Born criteria. Electronic structure analysis reveals that the pristine material exhibits a bandgap (E g) of 2.69 eV, while Be@Ba significantly reduces it to 0.58 eV, while other dopants maintain moderate gaps in the range of 1.85-2.63 eV. Alongside this, the work function exhibits a non-monotonic enhancement from 5.71 eV (pristine) to 6.11 (Be@Ba), 6.36 (Mg@Ba), 6.38 (Sr@Ba), and 6.25 eV (Ra@Ba), while CA@Ba attains the maximum value of 6.45 eV, indicating that surface dipole strengthening is governed by an optimal interplay of dopant size. Ultimately, thermoelectric performance is significantly enhanced upon doping, with improved electrical conductivity and reduced lattice thermal conductivity, resulting in a maximum figure of merit of 0.75/0.85 at 800 K for the Ra@Ba/Ca@Ba-doped structures.
More Related Videos
06:32A Simple, Low-cost, and Robust System to Measure the Volume of Hydrogen Evolved by Chemical Reactions with Aqueous Solutions
Published on: August 17, 2016
13:56Probe Type II Band Alignment in One-Dimensional Van Der Waals Heterostructures Using First-Principles Calculations
Published on: October 12, 2019
Related Concept Videos
02:42Valence Bond Theory
02:44The Born-Haber Cycle
01:26Radical Substitution: Hydrogenolysis of Alkyl Halides with Tributyltin Hydride
The bonds formed in this reaction are stronger than the bonds broken, making it energetically favorable. The reaction follows a radical chain mechanism similar to radical halogenation reactions,...
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human eye.