100-Fold Reductivity Enhancement of Nanoscale Zero-Valent Iron After 1-Year Aging in Water via Regulating Corrosion

Yirong Wang1, Yi Luan1, Zhaowei Huang1

  • 1State Key Laboratory of Soil Pollution Control and Safety, Zhejiang Provincial Key Laboratory of Organic Pollution Process and Control, Key Laboratory of Environmental Pollution and Ecological Health of Ministry of Education, College of Environmental and Resource Sciences, Zhejiang University, Hangzhou, China.

Angewandte Chemie (International Ed. in English)
|August 23, 2026
PubMed

Keywords:
aging timecorrosion reactionsnanoscale zero‐valent ironreductivitysurface modificationtransformation

More Related Videos

Generation of Zerovalent Metal Core Nanoparticles Using n-(2-aminoethyl)-3-aminosilanetriol08:12

Generation of Zerovalent Metal Core Nanoparticles Using n-(2-aminoethyl)-3-aminosilanetriol

Published on: February 11, 2016

The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight10:27

The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight

Published on: October 11, 2016

Related Concept Videos

Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...
Microbes and Other Elemental Cycles01:24

Microbes and Other Elemental Cycles

Microbial activity plays a pivotal role in the biogeochemical cycling of iron and manganese, especially at the redox gradients characteristic of stratified aquatic environments. These cycles are driven by microbial transformations between oxidized and reduced forms of the metals, allowing organisms to exploit them for metabolic energy and structural purposes.Iron Cycling Across Redox GradientsIn neutral, oxygen-rich surface waters, iron is predominantly found in its oxidized, insoluble ferric...