Biomedical Hydrogel Bio-Adhesive Based on Lactobionic Acid Conjugated Polyethylenimine and Oxidized Dextran with...

Background/Objectives: Tissue bio-adhesives have gained significant attention as efficient alternatives to conventional wound closures, which are often hindered by insufficient adhesion and poor biocompatibility. Methods: Inspired by nature's robust wet-adhesion strategies that use dynamic covalent interactions, we have reported a facilely fabricated hydrogel bio-adhesive based on lactobionic acid-conjugated polyethylenimine (LA-PEI) and oxidized dextran (ODex) via Schiff base linkages. Results: The prepared hydrogels exhibited three-dimensional interconnected porous networks, regulated swelling ratios, typical viscoelasticity, shear-thinning behavior, and self-healing ability. Notably, the swelling ratios of the hydrogels depended on composition, and OLP11 displayed the highest swelling ratio of over 1500%. The hydrogel bio-adhesives exhibited strong adhesion to various surfaces, including glass, metal, plastic, rubber, and wood, as well as to different chicken organs, including the heart, liver, spleen, and stomach. Furthermore, the hydrogels exhibited excellent ABTS radical-scavenging activity, effective intracellular reactive oxygen species (ROS) scavenging, and good hemocompatibility, with hemolysis ratios of all hydrogels close to 0%, below the threshold of 5%. After culturing with NIH 3T3 fibroblasts, the hydrogels demonstrated good cytocompatibility and promoted cell proliferation, with cell viabilities on day 3 reaching over 90%. Conclusions: This design yields multifunctional hydrogel bio-adhesives, showing strong promise for wound care and tissue repair applications.