Evaluation of Microstructure and Mechanical Properties of T6 Heat-Treated Al-Cu-Mg Aluminum Alloy Based on Laser...

At present, the detection methods for the microstructure and mechanical properties of aluminum alloys are mainly based on SEM, EBSD, TEM, tensile tests, and microhardness tests, which are time-consuming and destructive. In this paper, laser ultrasonic non-destructive detection is employed to obtain ultrasonic signals from Al-Cu-Mg aluminum alloy subjected to various heat treatment processes. The results reveal empirical correlations between the characteristic values of the ultrasonic signals and the material's state. Specifically, the characteristic values exhibit an inverse correlation with the precipitated phase content. When both the precipitated phase content and the average grain size vary significantly, distinct deviations in the characteristic values are observed, which can serve as indicators of microstructural changes. The extracted ultrasonic eigenvalues also show promising, empirically derived correlations with mechanical properties, with frequency-domain attenuation coefficients demonstrating relatively higher sensitivity based on fitting analyses within the current dataset. These observed variations are tentatively discussed as plausible consequences of grain boundary scattering and changes in matrix solid solution strengthening associated with precipitate dissolution. Overall, the findings suggest the potential of laser ultrasonics as a rapid non-destructive evaluation tool, providing a preliminary scientific basis for further development of methods to assess the microstructure and mechanical properties of Al-Cu-Mg alloys within the tested parameter space.