Microstructural and Surface Energy Evaluation of Concrete Coatings Modified with Methyl Ester and Stearic Acid

Robert Hunek1, Martyna Janek2, Wojciech Franus2

  • 1Doctoral School, Lublin University of Technology Nadbystrzycka 38B/406, 20-618 Lublin, Poland.

Materials (Basel, Switzerland)
|August 27, 2026
PubMed

Keywords:
coatingconcretecontact anglemethyl estermicrostructurestearic acid

More Related Videos

Applying Permanent, Robust Stenciled Patterns of Fine Particles to Elastomeric Surfaces07:12

Applying Permanent, Robust Stenciled Patterns of Fine Particles to Elastomeric Surfaces

Published on: July 8, 2025

Laser Micromachining for Polymer Surface Topography Design05:49

Laser Micromachining for Polymer Surface Topography Design

Published on: September 19, 2025

Related Concept Videos

Acid Attack on Concrete01:21

Acid Attack on Concrete

When acids come into contact with concrete, they initiate a chemical reaction that dissolves the hydrated cement paste. This process leads to softening and structural weakening of the concrete. This issue is commonly observed in environments such as chimneys, sewers, and industrial settings. The severity of the damage increases as the pH of the water interacting with the concrete drops below 6.5. In particular, a pH under 4.5 can cause significant concrete damage.
The rate at which hydrogen...
Waterproofing and Anti-Bacterial Admixtures in Concrete01:22

Waterproofing and Anti-Bacterial Admixtures in Concrete

Concrete's susceptibility to water absorption is due to the capillary action within the pores of its hydrated cement paste. This action draws water in, creating the need for waterproofing admixtures to prevent such penetration. The efficacy of these admixtures is contingent upon the water pressure, with variations arising from different conditions such as rain, capillary rise, or hydrostatic pressure in structures intended to hold water.
Waterproofing admixtures render concrete hydrophobic,...
Esters to Carboxylic Acids: Saponification01:25

Esters to Carboxylic Acids: Saponification

Esters can be hydrolyzed to carboxylic acids under acidic or basic conditions. Base-promoted hydrolysis of esters is a nucleophilic acyl substitution reaction in which esters react with an aqueous base, followed by an acid to give carboxylic acids. This reaction is also known as saponification because it forms the basis for making soaps from fats.
The reaction requires a base in stoichiometric amounts, which participates in the reaction and is not regenerated later. So, the base acts as a...
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
Effect of Sea Water on Concrete01:22

Effect of Sea Water on Concrete

Concrete exposed to seawater can undergo degradation like the dissolution of ettringite and gypsum, increasing the material's porosity and decreasing its strength. In contrast, the crystallization of salts within the concrete's pores can cause expansion, particularly above the waterline where evaporation occurs. Nonetheless, this expansion only happens when seawater, enabled by the concrete's permeability, manages to infiltrate the structure.
Concrete in areas between tide marks, which undergo...
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...