Fused Deposition Modeling (FDM) of polyether-ether-ketone (PEEK) dental implants: A systematic review of the effect...

This systematic review evaluated how FDM printing parameters influence mechanical behaviour and surface characteristics of 3D-printed PEEK and identified parameter combinations linked to the most favourable mechanical performance and surface quality.

An electronic search was conducted in: MEDLINE (Ovid), PubMed, Embase, Web of Science, Scopus, and Compendex (last update: January 2025). Studies that evaluated the effect of FDM printing parameters on mechanical and surface properties of PEEK were included. Outcomes comprised compressive, tensile, and flexural strengths, elastic modulus, fracture toughness, surface hardness, roughness, and wettability.

Of 4005 reports screened, 54 manuscripts were included. 92.6% (n = 50) of articles showed low risk-of-bias, while 7.4% (n = 4) showed medium risk-of-bias. Tensile strength was the most investigated mechanical parameter (78%), followed by elastic modulus (41%), flexural strength (30%), compressive strength (20%), and fracture toughness (6%). Surface roughness was the most evaluated surface property (30%), followed by hardness (17%) and wettability (6%). Across studies, higher printing temperatures, lower printing speed, thinner layer thickness, and maximum infill ratio in a horizontal printing orientation were associated with higher strengths, less warpage, increased accuracy, and improved surface quality.

Specific combinations of FDM printing parameters can significantly improve the mechanical and surface properties of PEEK. However, it is difficult to meet all the optimal conditions simultaneously. Thus, balancing between different parameters must be considered in practical production.