Towards microplastic bioremediation: Fungal degradation of pristine and pretreated high-density polyethylene and...

Microplastic (MP) contamination has become a significant ecological issue because of its enduring existence in the ecosystem and its possible negative impacts. Therefore, using degrading strategies to eliminate these stubborn polymers has been a subject of scientific research. However, the currently used degradation methods are relatively inefficient. Given the pervasiveness of High-Density Polyethylene (HDPE) and Polystyrene (PS) and their resistance to biodegradability, disposal strategies are critical and must be addressed. This manuscript examines the biodegradation of pristine and UV-treated HDPE and PS MPs by Aspergillus flavus species in minimal growth media over 70 days. The maximum weight loss observed at 70 days for pristine HDPE and PS in sole carbon source (SCS) media was (29.33 ± 0.28) % and (17.67 ± 0.35) %, respectively. Whereas, for UV-treated HDPE and PS MPs, the % weight reduction was (33 ± 0.21) % and (25 ± 0.19) %, respectively. UV-treated MPs exhibited greater weight reduction, as UV induced oxygenated functional groups enhance polymer susceptibility to enzymes, thereby promoting biodegradation. HDPE MPs typically show a higher proportion of particles in the lower size range compared to PS MPs. This assertion was based on the weight loss, particle size distribution, and SEM analysis. Furthermore, chemical changes were evaluated using Fourier transform Infrared Spectroscopy (FTIR) analysis, which also displayed chemical oxidation occurring during biodegradation. Liquid Chromatography-Mass Spectrometry (LC-MS) results indicate that UV pretreatment enhances biodegradability by promoting chain scission. These findings further suggest that this fungus's natural and ubiquitous occurrence in terrestrial and marine environments may actively contribute to MP biodegradation while requiring few nutrients.