Effect of Varying RuO2 (100) Thin-Film Stoichiometry on the Activity-Stability Compromise in the Oxygen Evolution
Ikenna Chris-Okoro1, Ghanashyam Gyawali1, Sheilah Cherono1
1Department of Mechanical Engineering, North Carolina A&T State University, Greensboro, North Carolina 27411, United States.
Abstract:
This study investigates the electrochemical properties of ruthenium dioxide RuO2 (100) thin films to understand the effect of varying oxygen deposition ambience on the activity-stability compromise and the degradation pathways consisting of the Lattice Oxygen Mechanism (LOM) and Adsorption Evolution Mechanism (AEM). Electrochemical evaluation of the RuO2 films in the oxygen evolution reaction (OER) in both alkaline and acidic media shows a lower overpotential for less oxygenated films than for more oxygenated films. Stability analysis reveals that, under alkaline conditions, the less oxygenated RuO2 thin-film samples experience a ∼16.5% reduction in current density, while the more oxygenated films experience a ∼9% reduction after 3 h. In acidic conditions, a higher current reduction of ∼21% was observed for the less oxygenated samples, whereas an improved current output of up to 17% was observed for the more oxygenated samples. The Ru dissolution trend for less oxygenated and more oxygenated films showed more than an order of magnitude variation under alkaline conditions and less than 1 order of magnitude under acidic conditions. Additionally, Ru metal dissolution increased by an average of 2 orders of magnitude under acidic conditions compared to alkaline conditions. Faradaic efficiency (FE) was considerably low for the more oxygenated films under both acidic and alkaline conditions. Based on the observed high current density, low overpotential, and high FE, we hypothesize that while LOM is operative in less oxygenated samples, AEM is operative in more oxygenated samples.
More Related Videos
Related Concept Videos
02:31Multi-Step Reactions
03:08Rate-Determining Steps
In a multistep reaction mechanism, one of the elementary steps progresses significantly slower than the others. This slowest step is called the rate-limiting step (or rate-determining step). A reaction cannot proceed faster than its slowest step, and hence, the rate-determining step limits the overall reaction rate.
The concept of rate-determining step can be understood from the analogy of a 4-lane freeway with a short-stretch of traffic-bottleneck caused due to...
02:50Catalysis
01:27Catalysis
02:55Temperature Dependence on Reaction Rate
Atoms, molecules, or ions must collide before they can react with each other. Atoms must be close together to form chemical bonds. This premise is the basis for a theory that explains many observations regarding chemical kinetics, including factors affecting reaction rates.
The collision theory is based on the postulates that (i) the reaction rate is proportional to the rate of reactant collisions, (ii) the reacting species collide in an orientation allowing contact between...
03:06Reaction Mechanisms
For instance, the decomposition of ozone appears to follow a mechanism with two steps: