Effect of cement pressure and bone strength on polymethylmethacrylate fixation

The effect of the quality of the bone and of the cement pressurization magnitude and duration on the fixation achieved with polymethylmethacrylate (PMMA) bone cement is studied in vitro. Seventy-one cement-bone interface specimens, prepared under various conditions of pressurization of low-viscosity bone cement, are tested in tension. The load at failure and the maximum cement penetration are measured to assess the fixation achieved, and the quality of the bone is assessed by determining the compressive strength of each of the bone specimens. Statistical analysis of the data indicates that the pressure magnitude is the most influential of the factors considered in the cement penetration behavior and in the development of failure load capacity. The duration of the pressure does not appear to be a significant factor. The cement penetration is a decreasing function of the bone strength, reflecting a decrease in the porosity and an increase in the area fraction. Although not directly measured in these tests, these latter bone properties are indirectly measured by the bone compressive strength. The effect of increasing bone strength on the failure load is nonlinear. The development of adequate failure load capacity is the result of a balance between the cement penetration allowed by the porosity of the bone and the inherent strength of the cancellous bone itself. Weak bone, although adequately penetrated by cement, cannot provide strong fixation. Stronger, denser bone limits cement penetration, but pressurization enhances development of failure load capacity through more complete infusion and interlocking of the cement in the available pore space. The strength of the fixation achievable for any bone is limited by the intrinsic strength of the bone.(ABSTRACT TRUNCATED AT 250 WORDS)