A preliminary investigation into a method of producing a bond between glass-ionomer cement and ceramics

O W Rogers, J R Griffith

    Australian Dental Journal
    |October 1, 1980
    PubMed

    Keywords:
    Dental bonding techniquesCeramic surface treatmentGlass-ionomer cement applicationsBond strength testing

    More Related Videos

    Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)08:29

    Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)

    Published on: January 7, 2019

    Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

    Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

    Published on: December 20, 2024

    Related Concept Videos

    Bonding and Strength of Aggregate01:12

    Bonding and Strength of Aggregate

    The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
    Porosity in Cement Paste01:18

    Porosity in Cement Paste

    The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
    The balance of water to cement in the mix is critical—it...