Flexural strength of an infused ceramic, glass ceramic, and feldspathic porcelain

In-Ceram material is a relatively new all-ceramic restorative material with improved properties that require research. The clinical selection of restorative materials is based on a number of parameters such as esthetics, fit, and strength. This study determined the flexural strength of In-Ceram system components and compared the core material with conventional feldspathic ceramics and with Dicor all-ceramic restorative material. Four-point flexural strength values of bend bars of each ceramic were 18.39 +/- 5.00 MPa for In-Ceram sintered alumina, 76.53 +/- 15.23 MPa for In-Ceram infusion glass, and 236.15 +/- 21.94 MPa for In-Ceram infused alumina core. Flexural strength of self-glazed feldspathic porcelain was 69.74 +/- 5.47 MPa, as-cast Dicor ceramic 71.48 +/- 7.17 MPa, and polished Dicor ceramic was 107.78 +/- 8.45 MPa.