Facilitated giga-seal formation with a just originated glass surface

A simple technique of tip preparation in patch pipettes is described, which facilitates giga-seal formation. The pipettes were fabricated from thick-walled borosilicate glass tubing (external diameter 2.0 mm, internal diameter 0.5 mm) and the tips could be repeatedly broken in the bath. The pipette resistance correspondingly fell in steps of 3-20 M omega from about 80 M omega to about 2 M omega (double concentrated Tyrode). Scanning electron microscopy showed that the tip obtained after breaking was fairly plain. These broken tips were especially appropriate for patch-clamping. In cardiac myocytes in 11 out of 26 patches with Na+ channel activity, giga-seals developed spontaneously, i.e. without suction. In these patches the amplitude of the mean current with depolarizing pulses to -40 mV was significantly higher in comparison with patches formed under negative pressure. It is concluded that spontaneously sealed patches are most likely of planar configuration and the Na+ channel activity exceeds that in suction-induced patches.