[Effects of inadequate cementing techniques on mechanical loading of bone cement]

Related Experiment Video

Updated: Nov 9, 2026

An Improved Mechanical Testing Method to Assess Bone-implant Anchorage
11:51

An Improved Mechanical Testing Method to Assess Bone-implant Anchorage

Published on: February 10, 2014

S Kahl, C Kranz, M Kulbach

    Biomedizinische Technik. Biomedical Engineering
    |December 1, 1993
    PubMed

    More Related Videos

    In situ Compressive Loading and Correlative Noninvasive Imaging of the Bone-periodontal Ligament-tooth Fibrous Joint07:09

    In situ Compressive Loading and Correlative Noninvasive Imaging of the Bone-periodontal Ligament-tooth Fibrous Joint

    Published on: March 7, 2014

    Related Concept Videos

    Soundness of Cement01:17

    Soundness of Cement

    The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create ettringite,...
    Microcracking in Concrete01:20

    Microcracking in Concrete

    Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
    Strength of Cement01:20

    Strength of Cement

    Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
    For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
    Bone Disorders01:29

    Bone Disorders

    Aging and its effect on bone remodeling is the most common cause of bone disorders. In young and healthy people, bone deposition and resorption happen at an equal rate to maintain optimal bone health.
    Bone deposition is also affected by the levels of sex hormones like estrogen and testosterone that promote osteoblast activity and bone matrix synthesis. When the level of these hormones decreases due to aging, it causes a reduction in bone deposition. As a result, bone resorption by osteoclasts...
    Behavior of Concrete Under Compressive Load01:23

    Behavior of Concrete Under Compressive Load

    Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
    As the concrete specimen fractures under...
    Creep in Concrete01:22

    Creep in Concrete

    Creep refers to the time-dependent increase in strain under a sustained load, excluding other time-dependent deformations associated with shrinkage, swelling, and thermal expansion in concrete. The primary mechanism behind creep involves the loss of physically adsorbed water from the calcium silicate hydrate within the hydrated cement paste. This process is further exacerbated by concrete's non-linear stress-strain relationship, microcrack development in the interfacial transition zone, and...