Fatigue behavior of zirconia hip joint heads: experimental results and finite element analysis

J M Drouin1, B Cales, J Chevalier

  • 1INSA, GEMPPM, URA341, Villeurbanne, France

Journal of Biomedical Materials Research
|February 1, 1997
PubMed

More Related Videos

Imaging of the Microstructural Failure Mechanism in the Human Hip08:43

Imaging of the Microstructural Failure Mechanism in the Human Hip

Published on: September 29, 2023

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

Related Concept Videos

Normal Strain under Axial Loading01:20

Normal Strain under Axial Loading

Normal strain under axial loading is an important concept in the field of mechanics of materials. Axial loading implies the application of a force along the axis of a material, like a column or bar. This force can either compress or stretch the material. In the context of axial loading, normal strain is the deformation experienced by the material in the direction of the loading force. It's calculated as the change in length divided by the original length of the material. This unitless ratio...
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
General Case of Eccentric Axial Loading01:12

General Case of Eccentric Axial Loading

Unsymmetrical bending occurs when the bending moment applied to a structural member does not align with its principal axis. This misalignment leads to complex stress distributions and deflection patterns that differ from symmetrical bending, which are essential for designing structures to withstand different loading conditions.
Consider a member subjected to equal and opposite forces that are applied along a line that does not coincide with the member's neutral axis. In unsymmetrical bending,...
Stresses under Combined Loadings01:23

Stresses under Combined Loadings

When analyzing a bent tube with a circular cross-section subjected to multiple forces, it is crucial to determine the stress distribution in order to maintain structural integrity under varied load conditions.
The process begins by slicing the tube at critical points and analyzing the internal forces and stress components at these sections, focusing on the centroid. Normal stresses, generated by axial forces and bending moments, are either compressive or tensile and vary across the section from...
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...