Surface characterization and biological properties study of silicone rubber membrane grafted with phospholipid as...

Poly(2-methacryloyloxyethyl phosphorylcholine) (pMPC) was grafted onto the surface of a silicon rubber (SR) membrane (pMPC-SR) by plasma induced grafted copolymerization (PIP). Argon plasma was used to activate the SR surfaces. Determination was also made of the influences of grafted copolymerization reaction time, reaction temperature, and monomer concentration on polymerization yield. The surface properties of SR were characterized by ATR-FTIR, ESCA, and SEM. In those analyses the ATR-FTIR spectra indicated that the pMPC grafted onto the SR surface at 1720 and 3300 cm(-1). The elemental composition and different carbon bindings on the surface of the SR were examined by ESCA. An increasing P1s/C1s value g was obtained in the grafted polymerization yield with a concentration of 0.05-0.5M of MPC in the isolated ethanol solution. The surface morphologies of pMPC-SR differed more than those of control and Ar plasma treated surfaces. The difference could have been caused by the homogeneous graft polymerization of pMPC onto the SR membrane. In the biological analyses, protein adsorption on pMPC-SR surfaces was reduced. The reduced level increased with an increase in the pMPC grafted amount. The epithelial cell attachment and growth onto these samples were suppressed. The blood compatibility for a series of pMPC-SR surfaces was examined by platelet adhesion. Blood platelet morphologies in contact with the high ratio of pMPC-SR surfaces were maintained, meaning that in this case the release reaction for platelets never occurred. Consequently, the high amount of pMPC-SR surface had excellent blood compatibility, further suggesting that prevention of adhesion, activation of platelets, and adsorption of blood protein could be achieved.