A liposomal hydrogel for the prevention of bacterial adhesion to catheters

The adhesion of bacteria to medical implants and the subsequent development of a biofilm frequently results in the infection of surrounding tissue and may require removal of the device. We have developed a liposomal hydrogel system that significantly reduces bacterial adhesion to silicone catheter material. The system consists of a poly (ethylene glycol)-gelatin hydrogel in which liposomes containing the antibiotic ciprofloxacin are sequestered. A poly (ethylene glycol)-gelatin-liposome mixture was applied to a silicone surface that had been pre-treated with phenylazido-modified gelatin. Hydrogel cross-linking and attachment to surface-immobilized gelatin was accomplished through the formation of urethane bonds between gelatin and nitrophenyl carbonate-activated poly (ethylene glycol). Liposomal hydrogel-coated catheters were shown to have an initial ciprofloxacin content of 185+/-16 microg cm(-2). Ciprofloxacin was released over seven days with an average release rate of 1.9+/-0.2 microg cm(-2) h(-1) for the first 94 h. In vitro assays using a clinical isolate of Pseudomonas aeruginosa established the antimicrobial efficacy of the liposomal hydrogel. A modified Kirby-Bauer assay produced growth-inhibition zone diameters of 39+/-1 mm, while bacterial adhesion was completely inhibited on catheter surfaces throughout a seven-day in vitro adhesion assay. This new antimicrobial coating shows promise as a prophylactic and/or treatment for catheter-related infection.