Controlling the Size, Shape and Stability of Supramolecular Polymers in Water
Published on: August 2, 2012
Control de conformación en la ciclización de polímeros supramoleculares enlazados por hidrógeno
A Tessa ten Cate1, Huub Kooijman, Anthony L Spek
1Laboratory of Macromolecular and Organic Chemistry, Eindhoven University of Technology, P.O. Box 513, 5600 MB Eindhoven, The Netherlands.
Journal of the American Chemical Society
|March 25, 2004
Resumen
Los grupos metilo en los monómeros supramoleculares promueven la formación de dímeros cíclicos y la polimerización. La longitud del enlace entre las unidades de enlace de hidrógeno muestra un efecto impar-par, permitiendo concentraciones críticas sintonizables para el diseño de polímeros.
Área de la Ciencia:
- Química supramolecular de las moléculas.
- La ciencia de los polímeros es la ciencia de los polímeros.
- Química orgánica es la química orgánica.
Sus antecedentes:
- Los derivados bifuncionales de 2-ureido-4[1H]-pirimidinonona (UPy) utilizan enlaces cuádruples de hidrógeno.
- Estos derivados pueden autoensamblarse en oligómeros cíclicos y polímeros supramoleculares en solución.
- La comprensión de los equilibrios de la cadena de anillos es crucial para el diseño de nuevos materiales.
Objetivo del estudio:
- Investigar los equilibrios de cadena de anillo de los monómeros UPy con enlaces de alquilo sustituidos por metilo.
- Determinar la influencia de los sustitutos de metilo y la longitud del enlace en la polimerización.
- Caracteriza la concentración crítica (CC) y la concentración de dímeros cíclicos de equilibrio (EDC).
Principales métodos:
- (1) Espectroscopia de RMN H para analizar las interacciones moleculares y los equilibrios.
- Viscometría para evaluar las propiedades de la solución y el grado de polimerización.
- Análisis de la concentración crítica (CC) y de la concentración del dímer cíclico de equilibrio (EDC).
Principales resultados:
- Los sustitutos de metilo mejoran la dimerización cíclica, aumentando tanto la EDC como la CC.
- Se observó un efecto impar-par en CC y EDC con el aumento de la longitud del enlace.
- La estructura y conformación de los monómeros tienen un impacto significativo en la polimerizabilidad.
Conclusiones:
- La metilación y la longitud del enlace son factores clave para controlar el autoensamblaje del monómero UPy.
- Los resultados proporcionan información sobre el ajuste de las concentraciones críticas para el diseño de polímeros supramoleculares.
- Los hallazgos contribuyen a la comprensión de los equilibrios de la cadena de anillos y las transiciones de la bobina aleatoria de hélice-hélice.
Más Videos Relacionados
Videos de Conceptos Relacionados
01:10Radical Chain-Growth Polymerization: Overview
Chain-growth or addition polymerization is successive addition reactions of monomers with a polymer chain. In radical chain-growth polymerization, the reaction proceeds via a free-radical intermediate. The free radical is formed from radical initiators, which spontaneously generate free radicals by homolytic fission. Organic peroxides (such as dibenzoyl peroxide, as shown in Figure 1) or azo compounds are popular radical initiators. A low concentration ratio of radical initiator to monomer is...
01:09Radical Chain-Growth Polymerization: Mechanism
The radical chain-growth polymerization mechanism consists of three steps: initiation, propagation, and termination of polymerization. The polymerization initiates when a free radical generated from the radical initiator adds to the unsaturated bond in the monomer. The unpaired electron of the free radical and one π electron in the unsaturated bond creates a σ bond between the free radical and the monomer. As a result, the other π electron in the unsaturated bond converts this species into the...
01:17Radical Chain-Growth Polymerization: Chain Branching
The skeletal structure of polymers synthesized via radical polymerization is always branched. For example, the polymerization of ethylene by radical polymerization results in a low-density grade of polyethylene with a heavily branched skeletal structure. Here, the radical site abstracts hydrogen from the growing chain, and the radical site shifts from the end (a primary carbon center) to anywhere within the growing chain (a secondary carbon center). Consequently, the part of the chain from the...
01:04Anionic Chain-Growth Polymerization: Mechanism
The mechanism for anionic chain-growth polymerization involves initiation, propagation, and termination steps. In the initiation step, a nucleophilic anion, such as butyl lithium, initiates the polymerization process by attacking the π bond of the vinylic monomer. As a result, a carbanion, stabilized by the electron‐withdrawing group, is generated. The resulting carbanion acts as a Michael donor in the propagation step and attacks the second vinylic monomer, which acts as a Michael acceptor.
00:57Cationic Chain-Growth Polymerization: Mechanism
The cationic polymerization mechanism consists of three steps: initiation, propagation, and termination. In the initiation step of the polymerization process, the π bond of a monomer gets protonated by the Lewis acid catalyst, which is formed from boron trifluoride and water. The protonation of the π bond generates a carbocation stabilized by the electron‐donating group. In the propagation step, the π bond of the second monomer acts as a nucleophile and attacks the generated carbocation,...
01:17Ziegler–Natta Chain-Growth Polymerization: Overview
Ziegler–Natta polymerization is another form of addition or chain‐growth polymerization used for synthesizing linear polymers over branched polymers. The catalyst used for polymerization is the Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, who developed it in 1953. This catalyst is an organometallic complex of titanium tetrachloride and triethyl aluminum, with the active form of the catalyst being an alkyl titanium compound. Using the Ziegler–Natta catalyst, high molecular...