Tapetes de nanofibras funcionalizados con MXeno Ti3C2Tx/PVDF electroactivo con alto potencial superficial para...

Fine PM_0.3-2.0 rapidly penetrates the respiratory system and causes health problems. Commercial filters remove 0.3 μm particles at ∼95% efficiency but impose high pressure drops that make breathing difficult. We fabricate a novel electrospun PVDF-Ti₃C₂T_x nanofiber mat for PM0.3-2.0 filtration. Where a high electric field stretched PVDF and PVDF-Ti₃C₂T_x solutions into ultrafine fibers that were collected as porous nanofibrous mats. PVDF was chosen for its electroactive behavior and high dielectric constant, enabling efficient electrostatic filtration. The incorporation of Ti₃C₂T_x MXene enhances surface charge density and interfacial polarization, strengthening particle-fiber interactions for improved submicron particulate capture. The mat delivers 99.99% filtration efficiency at 0.3 μm with a nominal pressure drop of 14.38 Pa/cm² and a quality factor of 0.05 Pa^-1. Filtration is governed by Van der Waals and enhanced dipole-dipole/induced-dipole interactions between fibers and particles. We attribute the improved performance to surface-terminating polar groups (O, OH, F) on Ti₃C₂T_x flakes that raise conductivity and surface potential, strengthening intermolecular forces (Si-OH, C-OH, C=O). PM_0.3 adsorption rates for pure Ti₃C₂T_x film, PVDF nanofiber, and PVDF-Ti₃C₂T_x are 52 μg/cm²/h, 12.1 μg/cm²/h, and 88.8 μg/cm²/h, respectively, consistent with interaction forces of 7 nN (PVDF/PM) and 22 nN (PVDF-Ti₃C₂T_x/PM). SKPM mapping shows nearly uniform electrostatic profiles with surface potentials of -7.32 to -8.44 V (PVDF) and -8.93 to 9.0 V (PVDF-Ti₃C₂T_x). Both mats remain hydrophobic by contact-angle analysis. Overall, this first-time PVDF-Ti₃C₂T_x nanofiber filter matches or exceeds commercial products, offering low ΔP and high efficiency for PM_0.3 removal. These results clarify capture mechanisms and support scalable use in breathable face masks.