メタルヒドリドの過剰な空白形成に関する第一原理の研究

Changjun Zhang1, Ali Alavi

  • 1Department of Chemistry, University of Cambridge, Lensfield Road, Cambridge CB2 1EW, UK.

Journal of the American Chemical Society
|July 7, 2005
PubMed
まとめ

金属ヒドリドの過剰空白 (SAV) は,エントロピーではなく,水素による電子構造の変化によって引き起こされます. 本研究は,様々なfcc金属水化物におけるSAV形成メカニズムを調査しています.

さらに関連する動画

Experimental Approaches for the Synthesis of Low-Valent Metal-Organic Frameworks from Multitopic Phosphine Linkers07:14

Experimental Approaches for the Synthesis of Low-Valent Metal-Organic Frameworks from Multitopic Phosphine Linkers

Published on: May 12, 2023

Determining Surface Areas and Pore Volumes of Metal-Organic Frameworks06:45

Determining Surface Areas and Pore Volumes of Metal-Organic Frameworks

Published on: March 8, 2024

関連する概念動画

Bonding in Metals02:32

Bonding in Metals

Metallic bonds are formed between two metal atoms. A simplified model to describe metallic bonding has been developed by Paul Drüde called the “Electron Sea Model”.
Metallic Solids02:37

Metallic Solids

Metallic solids such as crystals of copper, aluminum, and iron are formed by metal atoms. The structure of metallic crystals is often described as a uniform distribution of atomic nuclei within a “sea” of delocalized electrons. The atoms within such a metallic solid are held together by a unique force known as metallic bonding that gives rise to many useful and varied bulk properties.
All metallic solids exhibit high thermal and electrical conductivity, metallic luster, and malleability. Many...
Properties of Transition Metals02:58

Properties of Transition Metals

Transition metals are defined as those elements that have partially filled d orbitals. As shown in Figure 1, the d-block elements in groups 3–12 are transition elements. The f-block elements, also called inner transition metals (the lanthanides and actinides), also meet this criterion because the d orbital is partially occupied before the f orbitals.
Imperfections in Crystal Structure: Non-Stoichiometric Defects01:29

Imperfections in Crystal Structure: Non-Stoichiometric Defects

Non-stoichiometric defects refer to a type of defect in the crystal structure of a compound where the ratio of its constituent elements deviates from the ideal stoichiometric ratio. There are two main types of non-stoichiometric defects: metal excess defects and metal deficiency defects.Metal excess defects occur when there is a slight surplus of metal ions than what is required by the stoichiometric ratio of the compound. For example, heating a sodium chloride crystal in sodium vapor results...