Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

457

自己粘着性および自己エッチング性樹脂セメントの切断結合強度

Janet Kirilova1, Georgi Veselinov Iliev2, Sevda Yantcheva1

  • 1Department of Conservative Dentistry, Faculty of Dental Medicine, Medical University, 1000 Sofia, Bulgaria.

Journal of functional biomaterials
|August 27, 2025
PubMed
まとめ

セルフエッチング樹脂セメントは,間接的な美学的な復元を歯質に結合する際に,セルフアデシブセメントと比較して優れた切断結合強さを示した. 機能的モノマー10-メタクリロイロキシデシル二酸化水素 (10-MDP) は,粘着性を有意に高め,自己粘着性セメントは,より弱いデンチン結合を示した.

キーワード:
10-メタクリロオキシデシル二酸化水素間接的な美学的な修復樹脂セメント切断強度試験

さらに関連する動画

Application of Light-cured Dental Adhesive Resin for Mounting Electrodes or Microdialysis Probes in Chronic Experiments16:30

Application of Light-cured Dental Adhesive Resin for Mounting Electrodes or Microdialysis Probes in Chronic Experiments

Published on: July 30, 2007

15.5K
Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives08:40

Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives

Published on: May 17, 2020

3.1K

関連する概念動画

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
259
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
214
Chemical Bonds02:40

Chemical Bonds


Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons...
18.1K
Bond Energies and Bond Lengths02:49

Bond Energies and Bond Lengths

Stable molecules exist because covalent bonds hold the atoms together. The strength of a covalent bond is measured by the energy required to break it, that is, the energy necessary to separate the bonded atoms. Separating any pair of bonded atoms requires energy — the stronger a bond, the greater the energy required to break it.
25.8K
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
187