光ルミネッセンス増強による吸収性損傷部位の非破壊的同定

We present a non-destructive photoluminescence (PL) imaging strategy for probing damage growth behavior in fused silica under laser irradiation. Transient wide-field PL image measurements were conducted at varying excitation intensities to investigate the dynamics of radiative defect generation and annihilation in laser-induced damage sites. Our results reveal that, while low excitation intensities predominantly induce PL quenching due to defect annihilation, high-intensity excitation (>0.3 GW/cm² at 532 nm) triggers pronounced PL brightening (PLB), indicative of radiative defect generation. Image analysis demonstrates that PLB events are strongly correlated with subsequent damage growth (10 J/cm² at 351 nm), whereas overall PL intensity is not. No optically detectable morphological changes were observed during PLB, confirming the non-destructive nature of the technique. We propose that PLB arises from defect-assisted absorption of multiple photons at pre-existing absorptive centers, which enhances local absorptivity and initiates further defect formation. These findings establish PLB monitoring as a sensitive diagnostic tool for identifying damage sites with elevated absorptivity, enabling targeted maintenance and improved laser damage management in optical materials.