炭素繊維強化ポリエーテルエーテルケトンおよびチタン（Ti-6Al-4V）ロッキングプレート構成物の閾値ねじ込みトルク

Locking plate constructs are integral to modern fracture fixation, particularly in osteoporotic bone. Carbon-fibre reinforced polyetheretherketone (CFR-PEEK) plates offer a stiffness profile closer to cortical bone than titanium, potentially improving the mechanical environment for healing. However, the optimal insertion torque for locking screws in CFR-PEEK plates is unclear. This study investigated the influence of insertion torque on construct performance in CFR-PEEK plates compared to titanium alloy (Ti-6Al-4V) plates.

Locking screws (3.5 mm, Ti-6Al-4V) were inserted into Ti-6Al-4V and CFR-PEEK plates at six torque levels (0.5-3.0 Nm). Construct strength was assessed via axial push-out and cantilever bending tests. Video analysis was used to correlate insertion torque with screw rotation. Additional testing was performed on two-screw CFR-PEEK constructs at three torque levels (0.5, 1.5, 2.5 Nm).

Insertion torque was linearly related to screw rotation within the tested range (0.5-3.0 Nm). In CFR-PEEK single screw constructs, higher torque (≥2 Nm) improved push-out strength (p < 0.05), while 1.5 Nm yielded the highest cantilever strength (p < 0.05). Ti-6Al-4V constructs showed a similar trend. In two-screw CFR-PEEK constructs, no significant differences were found in performance across torques for either push-out or cantilever testing (p > 0.5).

Beyond an initial threshold (∼0.5 Nm), increased insertion torque did not consistently enhance construct performance. These findings indicate that moderate torques (∼1.5 Nm) optimise performance while reducing the risk of implant damage, support the mechanical reliability of CFR-PEEK plates.